MBR module component

1:PVDF hollow fiber composited membrane 2:High strength 3:High flux 4:Excellent anti-pollution abilities

1.Introduction of PVDF Composite Membrane

1.1The active layer of the composite membrane used in MBR module is formed by PVDF, which is highly evaluated for its exceptional chemical resistance. The characteristics of its PVDF composite membrane is shown as follows: 

Table 1 Characteristics of PVDF composite membrane 

Inner/Outer diameter	Coating layer thickness	Pure water flux (0.1MPa)	Mean pore size	Tensile strength	Structure (SEM)	MWCO
1.0/2.2mm	150μm	500~800LMH	0.03μm	>0.3MPa	Asymmetric Sponge	150,000

1.2Excellent oxidation resistance 

During the water treatment, microorganisms and organics are the main causes of UF membrane’s irreversible pollution, whereas oxidant cleaning is the most effective method to recover membranes’ flux in which outstanding chemical stability of PVDF can be presented.

1.3 High strength 

JF UF membrane’s tensile and compressive strength are greatly improved compared to similar products. Besides,it can sustain more than 50 KG strength because it is coated on a tubular macroporous support. Thus, our membrane can be applied to hostile environments and high strength cleaning conditions. 

1.4 Outer-pressure structure design 

Feed water requirements are relatively low due to the outer-pressure structure design, and requirements on particle size and suspended sediment concentration are lower. Compared with the inner-pressure structure, this structure greatly reduces potential pollution in membrane flow channels. 

1.5High water flux and rejection 

The initial membrane flux is almost 600-1000 L·m-2·h-1, and filtering precision can reach 0.03-0.05 μm while high flux is guaranteed. As a result, purer water can be obtained in spite of different feed water conditions. 

2. Technical parameters of JF4-11M/23M

Type	JF4-11M /23M
Dimension (mm)	806×1213 /806×2387
Membrane material	PVDF
Average pore size	0.03μm
Membrane area (m2)	11.0 /23.0
Potting material	epoxy resin/polyurethane
Outlet size (mm)	DN32
Design filtrate rate (m3/d)	4.4-5.5 /9.4-11.7

3.External size of JF4-11M/23M

  

( function(){ var aBigImageSrc = [ 'http://i00.i.aliimg.com/photo/v1/489557684_1/MBR_module_component.jpg' , 'http://i00.i.aliimg.com/photo/v1/489557684_2/MBR_module_component.jpg' , 'http://i00.i.aliimg.com/photo/v1/489557684_3/MBR_module_component.jpg' , 'http://i00.i.aliimg.com/photo/v1/489557684_4/MBR_module_component.jpg' , 'http://i00.i.aliimg.com/photo/v1/489557684_5/MBR_module_component.jpg' , 'http://i00.i.aliimg.com/photo/v1/489557684_6/MBR_module_component.jpg' ]; var oProductShow = new AE.run.minisite.productShow(); oProductShow.init( { 'aImgSrc': aBigImageSrc } ); } )(); MBR module component